Pure Epoxy Fusion Bonded Rust Red Color Powder Coating for Pipeline

• Customization: Available
• CAS No.: Fusion Bonded Epoxy Coating for Pipeline
• Formula: Fusion Bonded Epoxy Coating for Pipeline
• EINECS: Fusion Bonded Epoxy Coating for Pipeline
• Usage: Powder Coating, Fusion Bonded Epoxy Coating for Pipeline
• Color: Customized
• Appearance: Powder
• Method: Spray
• Components: Film Forming Matter
• Main Raw Material: Epoxy
• Level: Finish Coat
• Certification: ISO14001, RoHS, ISO9001
• Substrate: Steel
• Expiration Date: 1 year
• Formation Mechanism: Non Conversion Type
• Packaging: Carton
• Gel Temperature: 230°C
• Gel Time: 10~20minutes
• Shelf Life: 12months
• Leading Time: 15-21days
• Transport Package: Carton Box
• Specification: 20KG
• Trademark: FEIHONG
• Origin: China
• HS Code: 39070000
• Production Capacity: 450tons/Month

Product Description

Rust Red color FBE Fusion Bonded Epoxy Coating for Pipeline

Product Description

FBE Powder Coating with Excellent Corrosion Protection, Epoxy Resin Powder Coating for Oil Pipelines


Introduction
It's thermosetting epoxy powder is designed to protect pipelines from corrosion in the most demanding operating environments. This product has excellent properties of corrosion resistance and can be widely used in anti-corrosion for steel pipelines carrying oil, gas, water, and others.
This product has been certified to meet the requirements of the CSA Z245.20-18 standard.


Product Features
The film has high density and adhesion.
Excellent chemical corrosion resistance.
Excellent physical-mechanical properties.
Curing reaction speed can be adjusted according to the customer's request to satisfy the requirement of different spraying.


Powder Properties

Items		Acceptance Criteria	Test Standard
Color		Various	Visual Color-Pass
Cure Time (232±3ºC, min)		≤3min	CSA Z245.20.14 Section 12.1
Gel Time (205±3ºC, s)		10-30	CSA Z245.20.14 Section 12.2
Moisture Content, %		≤0.6	CSA Z245.20.14 Section 12.4
Particle Size	≥150µm, %	≤3.0	CSA Z245.20.14 Section 12.5
	≥250µm, %	≤0.2
Density (g/cm^3)		1.3-1.5	CSA Z245.20.14 Section 12.6
Thermal Properties	Tg1, ºC	50-70	CSA Z245.20.14 Section 12.7
	Tg2, ºC	≥100
	ΔH, J/g	35-60
Shelf Life @25ºC		12months
Theoretical Coverage		0.67-0.77 m^2/kg/mm

Film Properties

Items	Acceptance Criteria	Test Standard
Recommended Film Thickness	≥300um
Thermal Properties	ΔTg ≤3ºC	CSA Z245.20 Section 12.7
Cathodic Disbondment	24 Hours, -3.5V, 65ºC, ≤6.5mm 28 Days, -1.5 volt, 23ºC, ≤8mm 28 Days, -1.5 volt, 65ºC, ≤10mm 28 Days, -1.5 volt, 95ºC, ≤15mm	CSA Z245.20 Section 12.8
Porosity	Cross-section, Rating ≤3 Interface, Rating ≤3	CSA Z245.20 Section 12.10
Flexibility	bending, -30ºC, 3°, No Cracking	CSA Z245.20 Section 12.11
Impact Resistance	1.5J, -30ºC	CSA Z245.20 Section 12.12
2.5° Strained Coating	28d Cathodic disbondment	CSA Z245.20 Section 12.13
Adhesion, Rating	24 Hours, 75ºC, 1 Rating	CSA Z245.20 Section 12.14
	28d, 75ºC, 1-2 Rating
	28d, 95ºC, 1-2 Rating
Tabor Abrasion	Cs-17 1kg 5000r ≤300mg	ASTM D4060
Hardness	Shore hardness >80	ASTM D2240
Pull-Off Adhesion	>20MPa	ASTM D4541
Volume Resistivity	>1.0*10^15 Ω-cm	ASTM D257
Dielectric Strength	>30 MV/m	ASTM D149
Chemical Restraints	10% NaCl Solution, 30d, 23ºC  No blistering or disbondment	ASTM G20
	10% NaOH Solution, 30d, 23ºC  No blistering or disbondment
	10% HCl Solution, 30d, 23ºC  No blistering or disbondment
	20% Na2CO3 Solution, 30d, 23ºC  No blistering or disbondment
	5% HAc Solution, 30d, 23ºC  No blistering or disbondment
	30% H2SO4 Solution, 30d, 23ºC  No blistering or disbondment
	10% HNO3 Solution, 30d, 23ºC  No blistering or disbondment
	Methyl Alcohol 30d, 23ºC

Note: prepare specimens process

1. Abrasive blasting to Sa2.5 near-white metal with a surface profile of 50-100 microns. Then, clean the surface with high-pressure gas
2. Put the specimen into the oven (200ºC), and preheat for 40-60 min.
3. Spray the powder on the preheated specimen with an electrostatic spray gun, then put it in the oven, and keep 5-10 minutes at 200ºC 
4. The dry film thickness is 350±50µm.

Coating Reference
1. Application: Factors such as plant capability, specifications, and pipe construction or characteristics can affect application conditions. The recommended application temperature range is 200-220ºC.
2. Surface Preparation: Remove all surface contamination before abrasive blasting. Blast clean using steel grit to Sa2.5 near-white metal with a minimum surface profile of 2 mils/51 microns.


Precautions
1. All data are based on laboratory testing and practical experience.
2. It is recommended that the product should pass process evaluation before mass use, so as to avoid an unnecessary loss to customers due to various reasons such as process.


Package and Storage
1. The package is 25kg per box, lined with polyethylene plastic bags. In the course of shipment, it should be loaded or unloaded lightly and avoid direct sunlight and heat, and moisture.
2. The product should be stored in a cool, ventilated, dry room with a temperature below 25ºC and humidity below 65%.
3. Keep away from fire and heat and tide.
4. After use, it should be sealed in time to prevent powder from being polluted and damped.
5. Reduce the number of movements to avoid impact and pressure.
6. The maximum stacking height should not exceed 5 layers.