Electrostatic Tribo Spray Dry Powder Coating Paint for Metal Appliance

• CAS No.: 00-00-0
• Formula: 00-00-0
• EINECS: 00-00-0
• Usage: Powder Coating, Metal Spray Powder Coating
• Color: Ral Colors or Pantone Colors
• Appearance: Powder
• Model NO.: RAL
• Method: Spray
• Components: Resin, Pigment
• Main Raw Material: Epoxy Polyester
• Level: Finish Coat
• Certification: ISO14001, RoHS, ISO9001
• Substrate: Steel, Iron, Copper and Other Metals
• Expiration Date: 1 year
• Formation Mechanism: N/a
• Packaging: Carton
• Color on Basis: Ral or Pantone Chart
• Gloss: Glossy, Semi Glossy or Matt
• Finish: Smooth or Texture
• Mark: Neutrial or Designed by Customer
• Gun: Electrostatic or Tribo
• Certificate: ISO, RoHS and SGS
• Factory: We Have Our Own Powder Coating Factory
• Application: Shelf, Fence, Fan, Security Door and Others
• Annual Export Quantity: 3, 000 Tons
• 1 Container: 19 Tons
• Transport Package: 25kgs/Carton
• Specification: RAL colors or Pantone colors
• Trademark: EV
• Origin: China
• HS Code: 1111111
• Production Capacity: 4000tons

Product Description

Electrostatic tribo spray dry powder coating paint for metal appliance

Automobile fuel tank powder coating Description:
This series of products is saturated resin as the main component supplemented with the necessary pigments and additives, through the melt extrusion grinding, with excellent physical properties, chemical properties of thermosetting powder coating. This series of products can be produced according to the need to cure temperature 200 ° C products.

Specific gravity: 1.6 ~ 1.8g / c

CURING CONDITIONS

200 °C (work piece temperature), 10-15 minutes

Coating performance:
spray film thickness of normal products for the 60 ~ 80um. The results of the relevant tests are based on the requirements of the standard (or specific) of the substrate and pre-treatment under the premise may be with the customer before the actual treatment of the substrate to achieve the effect of different. And the test is obtained under laboratory conditions for reference only. Appearance Visual: close to the visual general refers to the natural light gloss visual: close to the visual or according to demand adjustment

Salt resistance: 500 hours of no change in the coating, cross-section single-sided corrosion <2mm. GB1771-91 Bondrite 1000 standard treatment iron plate, the coating thickness of 70um.
Wet heat resistance: 1000 hours, the film slightly lost light, <1 GB1740-79Bondrite 1000 standard treatment iron plate coating thickness 70um

Chemical resistance:
the general acid and alkali oil has a good resistance to normal temperature

AVERAGE COVERAGE

8-12 square meters / kg, thickness 60 microns (100% of the powder coating utilization rate)

PACKING

Outside carton lined with two layers of polyethylene bags, each containing 20 kg net weight.

STORAGE AND TRANSPORT

Stored in less than 30 °C, ventilated, dry, clean room, not near the fire source, heating, avoid direct sunlight, the product in the transport should be to prevent rain, sun, prolonged sun exposure.Storage products in line with the above conditions, since the date of production, effective storage period is 6 months.Over the storage period may be re-tested and the results were consistent with, can still be used.

HEALTH AND SAFETY

Coating powder is a non-toxic products, but should be avoided in the course of inhalation of dust.Proposed operators wear appropriate dust mask, glasses.If possible, try to avoid long-term skin contact with powder coating

 

Mechanical property
Testing items	Standards and methods	Inspecting index
Impact strength	GB/T1732-1993, AS3715 2.8	>50kg/cm
Bending resistance	GB/T1185-88, AS1580 402.1, ISO9227	Pass 2-5 millimeters
Adhesion CHECKED TEST	GB/T9286-88,2mm Cross cut, ISO2409	Pass100/100, passes 0 levels
Cupdrawing:Erichsen, ISO1520	Erichsen, ISO1520	Pass 3-7 millimeters
Pencil hardness	GB/T6739-86, Mitsubishi	Pass H-2H
Chemical resistance and weather resistance
Salt spray test	GB/T1771-91,500 hours	The cross section of corrosion less than 2MM
Hot and damp resistance test	GB/T17740-79(89),1000 hours	Without air bubbles, loses the light slightly
Acid resistance	10% CH3COOH, 240 hours	Without air bubbles, the surface without damage
Alkali resistance	10% NaOH, 240 hours	Without air bubbles, the surface without damage
Heat resistance	200degree,1 hour	The color change is lower than E=1.5
Solvent resistance	MEK24 hours soaked in solvent-free	Without air bubbles, the surface without damage
Uvioresistant	QUV-313,500 hours	Gloss higher than 80% lower than the Munsell color change level
Water tolerance of	2 hours	No bubble, not falling, losing light