Low Tempature 120 Degree Curing Semi Powder Coating for Radiator

• Usage: Powder Coating
• Color: Ral Color
• Appearance: Powder
• Method: Spray
• Components: Pigment
• Main Raw Material: Epoxy
• Model NO.: Ral3000
• Level: Finish Coat
• Certification: ISO14001, RoHS, ISO9001
• Substrate: Steel
• Expiration Date: 1 year
• Application: Electrostatic Spraying
• Colors: Ral Color
• Powder System: Epoxy Polyester
• Curing Condition: 180-200c/ 10-20minutes
• Transport Package: 25kg/Carton
• Specification: SGS
• Trademark: EVER
• Origin: China
• Production Capacity: 100t/Month

Product Description

Radiator powder coating main features:

1, excellent leveling, high gloss and high saturation
2, extremely high adhesion
3, good delay impact performance, coating after several years, still has excellent flexibility
4, can meet the requirements of post-forming, resistant to repeated bending
5, excellent oil resistance, oil resistance, can be repeatedly scrubbed

Radiator powder coating energy saving:
1, low temperature curing (120C*25min curing), can save 25% baking energy and reduce the cost of painting.
2, high powder rate spraying area, powder spraying area per kilogram can reach 8-9 square meters, saving 30% of raw materials.

STORAGE AND TRANSPORT

Stored in less than 30 °C, ventilated, dry, clean room, not near the fire source, heating, avoid direct sunlight, the product in the transport should be to prevent rain, sun, prolonged sun exposure.Storage products in line with the above conditions, since the date of production, effective storage period is 6 months.Over the storage period may be re-tested and the results were consistent with, can still be used.
 

HEALTH AND SAFETY

Coating powder is a non-toxic products, but should be avoided in the course of inhalation of dust.Proposed operators wear appropriate dust mask, glasses.If possible, try to avoid long-term skin contact with powder coating

Mechanical property
Testing items	Standards and methods	Inspecting index
Impact strength	GB/T1732-1993, AS3715 2.8	>50kg/cm
Bending resistance	GB/T1185-88, AS1580 402.1, ISO9227	Pass 2-5 millimeters
Adhesion CHECKED TEST	GB/T9286-88,2mm Cross cut, ISO2409	Pass100/100, passes 0 levels
Cupdrawing:Erichsen, ISO1520	Erichsen, ISO1520	Pass 3-7 millimeters
Pencil hardness	GB/T6739-86, Mitsubishi	Pass H-2H
Chemical resistance and weather resistance
Salt spray test	GB/T1771-91,500 hours	The cross section of corrosion less than 2MM
Hot and damp resistance test	GB/T17740-79(89),1000 hours	Without air bubbles, loses the light slightly
Acid resistance	10% CH3COOH, 240 hours	Without air bubbles, the surface without damage
Alkali resistance	10% NaOH, 240 hours	Without air bubbles, the surface without damage
Heat resistance	200degree,1 hour	The color change is lower than E=1.5
Solvent resistance	MEK24 hours soaked in solvent-free	Without air bubbles, the surface without damage
Uvioresistant	QUV-313,500 hours	Gloss higher than 80% lower than the Munsell color change level
Water tolerance of	2 hours	No bubble, not falling, losing light