properties make it a wide range of indoor applications,e.g.domestic appliances, home and office
furniture,light fixtures, shelvings, machinery, ceiling panels, switchboards etc.
Texture finish is also available for FH-GH .
GLOSS AND COLOR RANGE
Gloss levels range from semi gloss to high gloss:
40 - 90% and above depending on the end requirement .
Full color range is available.
APPLICATION SCHEDULE
Applied by : Electrostatic spraying devices
Curing schedule :15 minutes at 180ºC (metal temperature )
Optimal film thickness : 60 -90 um
POWDER PROPERTIES
Specific gravity : 1.3 - 1.75 (depend on colors)
Particle size distribution(Laser Particle size analyser) :Less than 5% above 100 um
50 - 65% above 32 um :
Average particle size : 35 - 45um
COATING PROPERTIES
Film thickness (ISO 2178) :
60 - 90 µm
Gloss (ISO 2813, 60º) :
>40%depending on the end requirement
In order to obtain optimal anti-corrosion properties, it is recommended to apply a chemical pretreatment
prior to powder coating application.
Ferrous metals(cold rolled steel, cast iron etc.): Iron or zinc phosphatation
Zinc surfaces(galvanized steel, zinc alloy) : Chromatation or zinc phosphatation
Aluminum alloys : Chromatation
STORAGE
Should be stored under dry conditions with good ventilation at a temperature not exceeding 30 C.
Storage period recommended should not exceed 6 months,in case exceeding 6 months without
affecting their free flowing properties, the powder will still have optimal characteristics.
Should be protected from excessive heat,humidity,water and contamination with foreign materials
such as powder, dust, dirt, etc.
Any leftover powder should be kept in an appropriate area that is cool and dry. Do not expose to the
air too long as the powder properties may deteriorate with the moisture.
Adhesion (ISO 2409) :
GT= 0
Pencil hardness(ASTM D3363 ) :
HB -H
Direct and reverse impact (ASTM D2794) :
> 50kg.cm
Salt spray Resistance ( ASTM B117, 500hrs)
(Maximum undercutting ,1 mm ):