Thermosetting Epoxy Polyester RAL8025/RAL9001/RAL9003 Powder Coating
Product detail
| Type |
Epoxy Powder Coating; Polyester Powder Coating; Epoxy-Polyester Powder Coating |
| Color | RAL&Pantone color |
| Surface Finish | Superior gloss and color retention |
| Particle Size | Average 32-42μm |
| Specific Gravity | 1.2-1.7g per cubic meter |
| Coverage | 8-12 square meters per Kg at 60-90 μm film thickness |
| film thickness | 90-110μm |
Instruction
| Application Voltage | 60-90 KV |
| Gun to Component Distance | 15-30CM |
| Curing Temperature | 180-200ºC,10 min-15 min |
Storage stability
|
♦Store in ventilated, dry, clean room, temperature < 25ºC |
♦Relative humidity 50-65% |
| ♦Away from direct sunlight, fire, heat | ♦For best performance, use within 6 months |
HEALTH AND SAFETY
Coating powder is a non-toxic products, but should be avoided in the course of inhalation of dust.Proposed operators wear appropriate dust mask, glasses.If possible, try to avoid long-term skin contact with powder coating
|
Mechanical property |
||
|
Testing items |
Standards and methods |
Inspecting index |
|
Impact strength |
GB/T1732-1993, AS3715 2.8 |
>50kg/cm |
|
Bending resistance |
GB/T1185-88, AS1580 402.1, ISO9227 |
Pass 2-5 millimeters |
|
Adhesion CHECKED TEST |
GB/T9286-88,2mm Cross cut, ISO2409 |
Pass100/100, passes 0 levels |
|
Cupdrawing:Erichsen, ISO1520 |
Erichsen, ISO1520 |
Pass 3-7 millimeters |
|
Pencil hardness |
GB/T6739-86, Mitsubishi |
Pass H-2H |
|
Chemical resistance and weather resistance |
||
|
Salt spray test |
GB/T1771-91,500 hours |
The cross section of corrosion less than 2MM |
|
Hot and damp resistance test |
GB/T17740-79(89),1000 hours |
Without air bubbles, loses the light slightly |
|
Acid resistance |
10% CH3COOH, 240 hours |
Without air bubbles, the surface without damage |
|
Alkali resistance |
10% NaOH, 240 hours |
Without air bubbles, the surface without damage |
|
Heat resistance |
200degree,1 hour |
The color change is lower than E=1.5 |
|
Solvent resistance |
MEK24 hours soaked in solvent-free |
Without air bubbles, the surface without damage |
|
Uvioresistant |
QUV-313,500 hours |
Gloss higher than 80% lower than the Munsell color change level |
|
Water tolerance of |
2 hours |
No bubble, not falling, losing light |
We offer free samples to you.