Coating Powder Primer for Heat Transfer

• Customization: Available
• Usage: Powder Coating
• Color: Ral Colors
• Model NO.: RAL COLORS
• Appearance: Powder
• Method: Spray
• Components: Pigment
• Main Raw Material: Polyester
• Level: Finish Coat
• Certification: ISO14001, RoHS, ISO9001
• Substrate: Steel
• Expiration Date: 1 year
• Application: Electrostatic Spraying
• Colors: Ral Color
• Powder System: Epoxy / Polyester
• Curing Condition: 180-200c/ 10-20minutes
• Transport Package: 25kg/Carton
• Specification: SGS
• Trademark: EVER
• Origin: China
• Production Capacity: 100t/Month

Product Description

Coating Powder  Primer for Heat Transfer

DESCRIPTION

• Sublimation Heat Transfer Powder Coating is also called Heat Transfer Powder Coating because of the process of heat transfer printing.This process is a sublimation process,which is a phisycal-chemical transition of a pattern from transfer paper or film to a substrate which is pre-coated with a special powder designed to be as the base color of this sublimation.
• Through this sublimation process countless effects and patterns such as woodgrain, marble, granite, fancies, pictures can be transferred on substrate surfaces.
• This series is available in a variety of color, gloss, finishes and shapes.
• The coating is flexible and non-sticky paper, so that the prefabricated steel could be coated with this products before post-forming.

SPECIFICATION

Product Name	powder coating
Color	RAL, Panton, Customized
Gloss level	high, sub, matt for choose
Surface Finish	smooth, hammer, etc
Applicatoin	Corona
Application Voltage	60-90  KV
Gun to Component Distance	15-30 CM
Film Thickness	80-90μm
Curing Temperature	190ºC(Object temperature) /15 minutes
Adhesion	Cross-cut (2mm),  no loss of adhesion
Impact Resistance	Direct & Indirect 50kg/cm
Pencil Hardness	2H
Flexibility	6mm Mandrel
Bending Test	3mm
Salt Spray Test	5% NaCl Solution for 500 hours - No change
Acid Resistance	5% HCL for 48 hours dip test - No change
Alkali Resistance	5% NaOH for 48 hours dip test - No change

STORAGE                                                                      
 
Under dry conditions,good ventilation at a temperature not exceeding 30 C,humidity<60%
2.Storage period recommended should not exceed 12 months,in case exceeding 12 months without affecting their free flowing properties, the powder will still have optimal characteristics.
3.Should be protected from excessive heat,humidity,water and contamination with foreign materials such as powder, dust, dirt, etc.
4.Any leftover powder should be kept in an appropriate area that is cool and dry. 
Do not expose to the air too long as the powder properties may deteriorate with the moisture.