Electrostatic Anti-Gassing Powder Coating Paints

• Customization: Available
• Application: Electrostatic Spraying
• Colors: Ral Color
• Model NO.: RAL
• Curing Condition: 180-200c/ 10-20minutes
• Transport Package: 25kg/Carton
• Specification: SGS
• Trademark: EVER
• Origin: China
• Production Capacity: 100t/Month

Product Description

Electrostatic Anti-gassing Powder Coating Paints

DESCRIPTION

• Specially designed to minimise the formation of bubbles caused by gas or moisture released from a porous substrate during cure.
• Ideal for galvanized steel, cast iron and aluminum.
• Porous substrates can be coated with almost no craters, pin holes,or air bubbles.
• Excellent chemical and stain resistance as well outstanding exterior durability.
• Available in a wide range of colors
• Environmentally friendly.

CHARACTERISTIC

• Chemistry: Epoxy/Polyester
• Gloss:60-95 gloss unit
• Particle size: Suitable for electrostatic spraying
• Specific gravity: 1.2-1.7g/cm3 
• Curing schedule(object temp.):150- 200ºC/10-15minutes
• Storage: Dry ventilation conditions below 25ºC(open boxes must be resealed tightly)
• Shelf life: 12months

Product Specification

Test Item	Test Method	Test Result
Film Thickness	ISO2360	60-80um
Pencil Hardness	ASTMD 3363	H-2H
Bending	ISO1519	≤10mm
Grid Test 1mm	ISO2409	0 CLASS
Impulse Test	ASTMD2794	Pass
Cupping Test	ISO1520	≥8mm
Heat Resistance 1000 hours	ISO6270-1	Popping<1mm
Salt Spray 1000 hours	ISO9227	Corrosion Spreading<1mm

STORAGE                                                                      
 
Under dry conditions,good ventilation at a temperature not exceeding 30 C,humidity<60%
2.Storage period recommended should not exceed 12 months,in case exceeding 12 months without affecting their free flowing properties, the powder will still have optimal characteristics.
3.Should be protected from excessive heat,humidity,water and contamination with foreign materials such as powder, dust, dirt, etc.
4.Any leftover powder should be kept in an appropriate area that is cool and dry. Do not expose to the air too long as the powder properties may deteriorate with the moisture.