Thermosetting Powder Paint High Glossy for Iron Gate Paint Colors

• Customization: Available
• CAS No.: N/a
• Formula: N/a
• EINECS: N/a
• Color: Black
• Appearance: Powder
• Main Raw Material: Epoxy
• Method: Spray
• Level: Finish Coat
• Certification: ISO14001, RoHS, ISO9001
• Substrate: Iron
• Components: Pigment
• Paint Film Property: Heat-Resisting Paint
• Formation Mechanism: Non Conversion Type
• Transport Package: Carton
• Specification: 25kgs/CTN
• Trademark: Feihong
• Origin: Jiangsu, China
• Production Capacity: 4800 Ton/ Year

Product Description

Contact Information:

Ms. Summer Yang | Sales Manager

 

Jinhu Color Powder Coating Co., Ltd.

Room 3-3102| No.56 Lingzhi Road| Xinghe World| Nanjing 210028 | China

 

 
 

Product Description:

Powder coating is a solid powdery synthetic resin coating composed of solid resin and pigments, fillers and additives. Unlike ordinary solvent-based paints and water-based paints, its dispersion medium is not solvent and water, but air. It has the characteristics of no solvent pollution, 100% film formation and low energy consumption.   

                                           

Application:

· Pipeline industry: anti-corrosion pipeline, oil pipeline, sewage pipe, vessel water pipe, gas pipe and valves etc.

· Metal furniture: Steel furniture, documents cabinets etc.

· Kitchen utensils: gas cylinder, gas cooker, kitchen ventilator etc.

· Construction industry: door lock, rebar and steel plate.

· Electrical industry: Electronic spare parts, winding coil, and insulation coating of the rotator etc.

 

Products Series:

· Available in standard curing and lower temperature curing

· Available in multi-colors, different gloss level such as high gloss ( above 90°), flat gloss( 70-80°), semi gloss ( 10-60°), matt( below 10°), particular color and gloss is made according to customers requirements.

· Available in various kinds of art textures, such as sandy, wrinkle, lanose grain, hammer tone, metallic effect etc.

 Physical Property:

Specific gravity: 1.11.8g/cm³ (varied with different color and gloss)

Particle size: average 10~38um, proportion 10~84um > 90%, it can be adjusted if special requirement is put forward to us in advance.

 

Curing Temperature:

Standard type: 180ºC/15 minutes

Or 160ºC/20 minutes, 200ºC/10 minutes if customer require

 

Pre-treatment:

The overall quality of the coating system is largely dependent on the type and quality of the pre-treatment. The recommended types of pre-treatment for the most frequently used substrates are:

 

Aluminium	Chromate conversion
Steel	Zinc phosphate
Zinc coated steel	Zinc phosphate or chromate conversion

 

Average Coating Rate:

A. Smooth Surface:
6-12/KG, film thickness 60μm (calculated according to 100 consuming of powder coating)

B. Texture Surface:

5-7/KG,film thickness is about 80-120μm

 

 Film Performance:

 

Test Item	Test standard and Method		Test index
Impact resistance	GB/T 1732 -1993	ISO6272	50kg·cm
Adhension(cross-cut)	GB/T 9286 - 1998	ISO2409	Class 0
Flexibility	GB/T 6742-1986	ISO1519	2mm
Pencil hardness	GB/T 6739-1996	ISO2815	1H-2H
Cupping test	GB/T 9753-1988	ISO1520	6mm
Salt spray resistance	GB/T 1771-1991	ISO7253	>400 Hours
Heat & humidity resistance	GB/T 1740-1979	ISO6270	>500 Hours,film gloss slightly lose
Note: 1. Above test are using 0.30mm thickness degreased, rust removed cold rolling steel plate, film thickness is 60-80um. 2. Film performance may slightly decrease with gloss decrease.